polished bright surface 431 Stainless Steel Round Bar
Delivery term:The date of payment from buyers deliver within days-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Shanghai
-
Validity to:
Long-term effective
-
Last update:
2017-10-16 14:31
-
Browse the number:
199
+
- Contactaixin:
Contactaixin:
sasa201609(Mr.)
-
Email:
telephone:
phone:
-
Area:
Shanghai
Address:No.588 ZhuYuan Road, MinHang District, Shanghai, China
-
Website:
http://www.sasametal.com/ http://sasa201609.getmesomeonegood.com/
+
Type 431 martensitic stainless steel,ASTM A276,431SS,AISI 431,T431 SS,UNS S43100,16Chromium with Ni Ferritic stainless steel bar include,410 Stainless Steel Round Bar,416 Stainless Steel Round Bar,420 Stainless Steel Round Bar,440C Stainless Steel Round Bar,ss 410 round bar
C% |
Si% |
Mn% |
P% |
S% |
Cr% |
Ni% |
N% |
Mo% |
Cu% |
≤0.20 |
≤1.0 |
≤1.0 |
≤0.040 |
≤0.030 |
15.0-17.0 |
1.25-2.50 |
-- |
- |
-- |
T*S |
Y*S |
Hardness |
Elongation |
|
(Mpa) |
(Mpa) |
HRB |
HB |
(%) |
≥415 |
≥207 |
-- |
-- |
≥45 |
Specifications of 431 ss bar:
| Standard | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311,DIN 1654-5,DIN 17440,KS D3706,GB/T 1220 |
Material |
201,202,205,XM-19 etc. |
Surface |
Bright,Polishing,Pickled,Peeled,Black,Grinding,Hairline etc |
Technology |
Cold Drawn,Hot Rolled,Forged |
Specifications |
Size: 3mm~400mm |
Tolerance |
H9, H11, H13, K9, K11, K13 or as required |
More grade details of stainless steel shafts:
| Type | Grade |
Grade |
Chemical Component % |
||||||||||
C |
Cr |
Ni |
Mn |
P |
S |
Mo |
Si |
Cu |
N |
Other |
|||
Austenitic stainless steel |
201 |
1Cr17Mn6Ni5N |
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50－7.50 |
≤0.060 |
≤0.030 |
- |
≤1.00 |
- |
≤0.25 |
- |
201L |
03Cr17Mn6Ni5N |
≤0.030 |
16.00-18.00 |
3.50-5.50 |
5.50－7.50 |
≤0.060 |
≤0.030 |
≤1.00 |
≤0.25 |
||||
202 |
1Cr18Mn8Ni5N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
≤0.060 |
≤0.030 |
≤1.00 |
- |
≤0.25 |
－ |
||
204 |
03Cr16Mn8Ni2N |
≤0.030 |
15.00-17.00 |
1.50-3.50 |
7.00-9.00 |
0.15-0.30 |
|||||||
1Cr18Mn10Ni5Mo3N |
≤0.10 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
2.80-3.50 |
0.20-0.30 |
|||||||
2Cr13Mn9Ni4 |
0.15-0.25 |
12.00-14.00 |
3.70-5.00 |
8.00-10.00 |
|||||||||
2Cr15Mn15Ni2N |
0.15-0.25 |
14.00-16.00 |
1.50-3.00 |
14.00-16.00 |
0.15-0.30 |
||||||||
1Cr18Mn10Ni5Mo3N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
≤0.060 |
≤0.030 |
2.8-3.5 |
≤1.00 |
- |
0.20-0.30 |
- |
||
301 |
1Cr17Ni7 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
≤0.065 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
302 |
1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
303 |
Y1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.20 |
≤0.030 |
1) |
≤1.00 |
- |
- |
- |
|
303se |
Y1Cr18Ni9Se |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.20 |
≤0.030 |
- |
≤1.00 |
- |
- |
Se≥0.15 |
|
304 |
0Cr18Ni9 |
≤0.07 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
304L |
00Cr19Ni10 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
304N1 |
0Cr19Ni9N |
≤0.08 |
18.00-20.00 |
7.00-10.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
0.10-0.25 |
- |
|
304N2 |
0Cr18Ni10NbN |
≤0.08 |
18.00-20.00 |
7.50-10.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
0.15-0.30 |
Nb≤0.15 |
|
304LN |
00Cr18Ni10N |
≤0.030 |
17.00-19.00 |
8.50-11.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
0.12-0.22 |
- |
|
305 |
1Cr18Ni12 |
≤0.12 |
17.00-19.00 |
10.50-13.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
309S |
0Cr23Ni13 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
310S |
0Cr25Ni20 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
316 |
0Cr17Ni12Mo2 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
- |
- |
|
1Cr18Ni12Mo2Ti6) |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.80-2.50 |
≤1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
||
0Cr18Ni12Mo2Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.80-2.50 |
≤1.00 |
- |
- |
Ti5*C%-0.70 |
||
316L |
00Cr17Ni14Mo2 |
≤0.030 |
16.00-18.00 |
12.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
- |
- |
|
316N |
0Cr17Ni12Mo2N |
≤0.08 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
0.10-0.22 |
- |
|
316N |
00Cr17Ni13Mo2N |
≤0.030 |
16.00-18.50 |
10.50-14.50 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
0.12-0.22 |
- |
|
316J1 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
17.00-19.00 |
10.00-14.50 |
≤2.00 |
≤0.035 |
≤0.030 |
1.20-2.75 |
≤1.00 |
1.00-2.50 |
- |
- |
|
316J1L |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
17.00-19.00 |
12.00-16.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.20-2.75 |
≤1.00 |
1.00-2.50 |
- |
- |
|
317 |
0Cr19Ni13Mo3 |
≤0.12 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
3.00-4.00 |
≤1.00 |
- |
- |
- |
|
317L |
00Cr19Ni13Mo3 |
≤0.08 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
3.00-4.00 |
≤1.00 |
- |
- |
- |
|
1Cr18Ni12Mo3Ti6 |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.50-3.50 |
≤1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
||
0Cr18Ni12Mo3Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.50-3.50 |
≤1.00 |
- |
- |
Ti5*C%-0.70 |
||
317J1 |
0Cr18Ni16Mo5 |
≤0.040 |
16.00-19.00 |
15.00-17.00 |